| Aluminum extrusion glass door and window frame | |
| Material | Aluminum Alloy 6061,6063,6065 |
| Temper | T4,T5,T6 |
| Surface Treatment | Anodizing with colors ODM, Powder coated, Electrophoresis,Wooden grain etc. |
| Wall Thickness | >0.6mm or Customized |
| Length | <=6m or Customized |
| Color | Silver, Gold, Champagne,Bronze, White ,Black etc. |
| Packing | Usually by PE film, EPE foam, Kraft paper ,etc. |
| Container | 20ft container collect 12-20 tons |
| Delivery Time | Within 15-20days after payment |
| Mould | base on your drawings or our available mould |
| Applications | Aluminium door and window profile,aluminium curtain wall ,industrial aluminium materials |
| Port | Always at Shanghai Port ,or as request |
| Payment Terms | Always T/T,Alibaba Trade Assurance or LC. |
| Shape | Square, Round, Flat, or according to customers' drawings |
| Deep processing | cutting, drilling, bending etc |
| Quality Control | 1.Inspection at Site. |
| 2.Inspection Before Shipping. | |
| 3.Testing Machine. | |
| New Molding | 7-10days depend on design and drawings |
| Certification | ISO9001,CNAS,BV |
| Feature | High corrosion-resistance, weather-resistance, heat-resistance, alkali-resistance |
| Table Chemical Composition of Aluminum Alloy |
| Alloy | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Other(each) | Other(totall) | Al |
| 6061(%) | 0.40-0.80 | <=0.7 | 0.15-0.40 | <=0.15 | 0.8-1.2 | 0.04-0.35 | <=0.25 | <=0.15 | <=0.05 | <=0.15 | Reminder |
| 6063(%) | 0.20-0.60 | <0.35 | <0.10 | <0.10 | 0.45-0.9 | <0.10 | <0.10 | <0.10 | <0.05 | <0.05 | Reminder |
| Oxidizzation of Aluminum Profile Finishing |
| Film Thickness Class | Averg Film Thickness | Part Film Thickness |
| AA10 | 10 | 8 |
| AA15 | 15 | 12 |
| AA20 | 20 | 16 |
| AA25 | 25 | 20 |
| Note:The anodized of goods is generally supplied in grade AA10 or is controlled according to clients request |
| Alloy | State | Tensile Strength Test | Hardness Test | |||||
| Tensile Strength | Non-proportional stretching stress | Stretching rate | Pattem thickness | |||||
| (Mpa) | (Mpa) | mm | HV | HW | ||||
| >= | ||||||||
| 6063 | T5 | 160 | 110 | 8 | 0.8 | 8 | ||
| T6 | 205 | 180 | 8 | ~ | ~ | ~ | ~ | |
| 6061 | T4 | 180 | 110 | 16 | ~ | ~ | ~ | ~ |
| T6 | 265 | 245 | 8 | ~ | ~ | ~ | ~ | |
| Note :The stretching rate can not be measured if the thickness of the taken part from the section is less than 1.2 mm | ||||||||